Zr-based metallic glass thin film coating for fatigue-properties improvement of 7075-T6 aluminum alloy

Y. Z. Chang, P. H. Tsai, J. B. Li, H. C. Lin, J. S.C. Jang, C. Li, G. J. Chen, Y. C. Chen, J. P. Chu, P. K. Liaw

研究成果: 雜誌貢獻期刊論文同行評審

17 引文 斯高帕斯(Scopus)

摘要

In order to improve the fatigue life of high strength aluminum alloy, a protection coating with 200 nm Zr-based metallic glass thin film (MGTF) coupled with 50 nm titanium thin film buffer layer was coated on the 7075-T6 aluminum alloy by DC sputtering. The results of four-point-bending fatigue test revealed that the fatigue life of 7075-T6 aluminum alloy with Zr-based MGTF could be improved by 30 times at a stress level of 250 MPa. The improvement of Zr-based MGTF coated samples in fatigue limit was 235 MPa (56.7% increase) in comparison with 150 MPa for the uncoated samples. The superior mechanical properties of Zr-based MGTF, such as high strength and good bending ductility, lower surface roughness, good adhesion between the film and the substrate, and high compressive residual stress are the key factors to improve the fatigue resistance of the coated aluminum alloy.

原文???core.languages.en_GB???
頁(從 - 到)331-334
頁數4
期刊Thin Solid Films
544
DOIs
出版狀態已出版 - 1 10月 2013

指紋

深入研究「Zr-based metallic glass thin film coating for fatigue-properties improvement of 7075-T6 aluminum alloy」主題。共同形成了獨特的指紋。

引用此