Thermal stability and mechanical properties of spray-formed and melt-spun Al89la6Ni5 metallic glass matrix composites

M. L. Ted Guo, Chi Y.A. Tsao, K. F. Chang, J. C. Huang, J. S.C. Jang

研究成果: 雜誌貢獻期刊論文同行評審

7 引文 斯高帕斯(Scopus)

摘要

A spray-formed Al89La6Ni5 metallic glass matrix composite plate was obtained in thickness of 1 mm and diameter of 200 mm, comprising over 64% primary crystals {e.g. Al11La3) uniformly dispersed in the glass matrix. The microstructure can not be achieved by annealing corresponding amorphous precursor. The crystals existing in the glass matrix were found to increase the hardness of the composite. Through nanoindentation test, the hardness and modulus of the composite at ambient temperature were found superior than its amorphous ribbon counterpart. The hardness of the composite was estimated with the rule of mixture from the constituents to be 4.4 GPa, which agreed well with the nanoindentation results. From loss modulus measurement and TMA test at elevated temperatures, a weak T8 signal in the range of 213-240°C was revealed in the as-spray-formed composite. Furthermore, the dimension shrinkage of the composite was only 0.5% during the TMA test, which is much smaller than that of amorphous ribbon counterpart by up to 20%. The enhanced hardness by constituent second phases and the dimension stability of the composite are associated with their inherent microstructure, the primary crystals in particular.

原文???core.languages.en_GB???
頁(從 - 到)1717-1721
頁數5
期刊Materials Transactions
48
發行號7
DOIs
出版狀態已出版 - 7月 2007

指紋

深入研究「Thermal stability and mechanical properties of spray-formed and melt-spun Al89la6Ni5 metallic glass matrix composites」主題。共同形成了獨特的指紋。

引用此