The proton conduction and hydrogen permeation characteristic of Sr(Ce0.6Zr0.4)0.85Y0.15O3-δ ceramic separation membrane

I. Ming Hung, Yen Juin Chiang, Jason Shian Ching Jang, Jing Chie Lin, Sheng Wei Lee, Jeng Kuei Chang, Chi Shiung Hsi

研究成果: 雜誌貢獻期刊論文同行評審

40 引文 斯高帕斯(Scopus)

摘要

In this study, proton-conducting Sr(Ce0.6Zr0.4)0.85Y0.15O3-δ perovskite is synthesized using the citrate-ethylenediaminetetraacetic acid (EDTA) complexing method. The crystal structure, sintering behavior, coefficient of thermal expansion (CTE), electrical conductivity, electrochemical performance and hydrogen permeation of the Sr(Ce0.6Zr0.4)0.85Y0.15O3-δ is determined for various atmospheres and partial pressures of water. Sr(Ce0.6Zr0.4)0.85Y0.15O3-δ is extremely dense after sintering at 1450°C for 6h. The structure of the Sr(Ce0.6Zr0.4)0.85Y0.15O3-δ does not change after heat treatment in a hydrogen atmosphere at a partial pressure of water of 4.93×10-2 atm. The CTE of the Sr(Ce0.6Zr0.4)0.85Y0.15O3-δ at temperature of 100-900°C is 11.4×10-6K-1. The electrical conductivity of the sample is 0.012Scm-1 at 900°C. The hydrogen permeation flux increases from 0.1 to 0.184mmolmin-1cm-2 as the temperature increases from 500°C to 800°C.

原文???core.languages.en_GB???
頁(從 - 到)163-170
頁數8
期刊Journal of the European Ceramic Society
35
發行號1
DOIs
出版狀態已出版 - 1 1月 2015

指紋

深入研究「The proton conduction and hydrogen permeation characteristic of Sr(Ce0.6Zr0.4)0.85Y0.15O3-δ ceramic separation membrane」主題。共同形成了獨特的指紋。

引用此