The kinetics of H2 adsorption on supported ruthenium catalysts

Hsin Yu Lin, Yu Wen Chen

研究成果: 雜誌貢獻期刊論文同行評審

46 引文 斯高帕斯(Scopus)

摘要

Ruthenium catalysts supported on SiO2, Al2O 3 and TiO2 were prepared by the impregnation method. Temperature-programmed desorption (TPD) method was applied to investigate the kinetics of hydrogen adsorption/desorption on these catalysts. All the TPD results show two-peak profile, except Ru/SiO2. The low-temperature peak was assigned to the hydrogen adsorbed on the Ru metal. The high-temperature peak was attributed to the spillover of hydrogen atoms from metal to the support. Both are activated process. The amount of adsorbed hydrogen increased with increasing adsorption temperature, and the maximum adsorption occurs at above 200°C. The activation energy of adsorption is a function of catalyst support and the reduction temperature. It decreases in the order of Ru/TiO 2 (500°C reduction)>Ru/Al2O3>Ru/ TiO2 (300°C reduction)>Ru/SiO2. The results demonstrated that the strong metal-support interaction exerted on Ru/TiO 2 would suppress hydrogen chemisorption at room temperature due to its high activation energy. However, hydrogen chemisorption on Ru/TiO 2 was not suppressed at high temperature. One is able to measure the Ru dispersion by adsorption of hydrogen at high temperature.

原文???core.languages.en_GB???
頁(從 - 到)283-290
頁數8
期刊Thermochimica Acta
419
發行號1-2
DOIs
出版狀態已出版 - 10 9月 2004

指紋

深入研究「The kinetics of H2 adsorption on supported ruthenium catalysts」主題。共同形成了獨特的指紋。

引用此