Synthesis of Mixed-Ligand Zeolitic Imidazolate Framework (ZIF-8-90) for CO2 Adsorption

Yu Te Liao, Saikat Dutta, Ching Hsuan Chien, Chien Chieh Hu, Fa Kuen Shieh, Chia Her Lin, Kevin C.W. Wu

研究成果: 雜誌貢獻期刊論文同行評審

38 引文 斯高帕斯(Scopus)

摘要

Microporous metal–organic frameworks (MOFs) exhibit advantages on gas adsorption and catalysis of small molecules owing to high surface area and suitable pore size. One of the members in MOF, zeolitic imidazolate framework (ZIF), has attracted much attention in recent days, and different kinds of ZIFs had been synthesized with single organic linker. However, only few reports discussed the effect of mixed linkers. In this research, we synthesized mixed linker ZIF structure, ZIF-8-90. Different mole percentage of 2-methylimidazole and 2-imidazolecarboxaldehyde were mixed together to form ZIF-8-90 X %. We found that DMF had good effect on controlling the particle size but reducing the productivity ratio. The ZIF-8-90 X % NPs had different physical properties, such as surface area, pore size distribution and gas adsorption. The results showed that ZIF-8-90 30 and 50 % were the better adsorbents for CO2 adsorption (2.37 and 2.82 mol/g, respectively) at room temperature, as compared with other microporous framework, MIL-series, HKUST-1, ZIF-100.

原文???core.languages.en_GB???
頁(從 - 到)251-258
頁數8
期刊Journal of Inorganic and Organometallic Polymers and Materials
25
發行號2
DOIs
出版狀態已出版 - 3月 2015

指紋

深入研究「Synthesis of Mixed-Ligand Zeolitic Imidazolate Framework (ZIF-8-90) for CO2 Adsorption」主題。共同形成了獨特的指紋。

引用此