Synthesis, crystal structure, and magnetic susceptibilities of CsFeP2O7 and RbFeP2O7

Edita Dvoncova, Kwang Hwa Lii

研究成果: 雜誌貢獻期刊論文同行評審

25 引文 斯高帕斯(Scopus)

摘要

Two new ternary iron(III) diphosphates, CsFeP2O7 and RbFeP2O7, have been prepared and the structure of the Cs compound was determined from single-crystal X-ray diffraction data. Base on powder X-ray diffraction RbFeP2O7 adopts the same structure type as that of the Cs compound. CsFeP2O7 crystallizes in the monoclinic space group P21/c with a = 7.684(3), b = 9.937(3), c = 8.378(3) Å, β = 104.84(3)°, V = 618.4(4) Å3, Z = 4, and R = 0.048. The structure consists of intersecting tunnels running along the [001] and [110] directions, and the Cs+ cations are located at the intersection of these tunnels. The framework is built up from corner-sharing FeO6 octahedra and P2O7 groups. CsFeP2O7 is isostructural with KFeP2O7. Variable-temperature powder magnetic susceptibility data exhibit an antiferromagnetic transition at TN ∼ 25 K.

原文???core.languages.en_GB???
頁(從 - 到)279-286
頁數8
期刊Journal of Solid State Chemistry
105
發行號1
DOIs
出版狀態已出版 - 7月 1993

指紋

深入研究「Synthesis, crystal structure, and magnetic susceptibilities of CsFeP2O7 and RbFeP2O7」主題。共同形成了獨特的指紋。

引用此