Synthesis and characterization of nano-sized zeolites

Cha Chin Wu, Yu Wen Chen

研究成果: 雜誌貢獻期刊論文同行評審

1 引文 斯高帕斯(Scopus)

摘要

Synthesis of zeolite ZSM-5 and silicalite-1 by hydrothermal crystallization of clear supersaturated homogeneous synthesis mixture has been achieved. The influence of the templates, synthesis temperature, synthesis time and SiO2/Al2O3 ratio on the properties of the nano-sized zeolite has been investigated. The properties of the samples were characterized by X-ray powder diffraction, N2 adsorption/desorption, scanning electron microscopy, and transmission electron microscopy. The results show that the temperature at 170°C was favorable to synthesize the nano-size zeolites. The use of tetrapropylammonium hydroxide as the template in the hydrothermal synthesis conditions employed was favorable to form nanozeolite than tetramethylammonium hydroxide. The synthesis time also plan an important role. 1 day was required to obtain a fully crystallized product. The longer crystallization time would produce bigger particles. A decrease in Al2O3 content would decrease the crystallite size. The nanosize ZSM-5 and silicalite with crystallite size of 150 nm have been successfully synthesized.

原文???core.languages.en_GB???
頁(從 - 到)435-445
頁數11
期刊Journal of the Chinese Institute of Chemical Engineers
35
發行號4
出版狀態已出版 - 7月 2004

指紋

深入研究「Synthesis and characterization of nano-sized zeolites」主題。共同形成了獨特的指紋。

引用此