Synthesis and characterization of cubic periodic mesoporous organosilicas with a high loading of disulfide groups

Po Jui Chiu, Shanmugam Vetrivel, Anthony S.T. Chiang, Hsien Ming Kao

研究成果: 雜誌貢獻期刊論文同行評審

15 引文 斯高帕斯(Scopus)

摘要

Well ordered cubic periodic mesoporous organosilicas (PMOs) with the SBA-1 motif containing a high loading of disulfide groups have been synthesized by simple co-condensation of bis[3-(triethoxysilyl) propyl]disulfide (BTEPDS) and tetraethoxysilane (TEOS) using the cationic surfactant cetyltriethylammonium bromide (CTEABr) as the template under acidic conditions. The materials thus obtained exhibited ordered and uniform mesopores up to 50 mol% of BTEPDS (based on silica) in the initial mixture. The successful incorporation of disulfide groups into the ordered mesopores was confirmed by 29Si and 13C solid-state NMR spectroscopy. These disulfide-functionalized PMO materials showed good adsorption efficiency for Hg2+ ions. The successful conversion of the disulfide moiety to sulfonic acid functionality was also demonstrated by a simple post-oxidation method using hydrogen peroxide.

原文???core.languages.en_GB???
頁(從 - 到)489-494
頁數6
期刊New Journal of Chemistry
35
發行號2
DOIs
出版狀態已出版 - 2月 2011

指紋

深入研究「Synthesis and characterization of cubic periodic mesoporous organosilicas with a high loading of disulfide groups」主題。共同形成了獨特的指紋。

引用此