Sm2O3 composite PEO solid polymer electrolyte

Peter P. Chu, M. Jaipal Reddy

研究成果: 雜誌貢獻期刊論文同行評審

95 引文 斯高帕斯(Scopus)

摘要

A novel lithium composite solid polymer electrolyte based on a polymer, poly(ethylene oxide) (PEO), and a rare earth oxide, Sm2O3, is reported. The incorporation of lithium salt and samarium oxide to PEO shows a dramatic modification of surface morphology. Scanning electron microscopy (SEM) shows that at a low Sm2O3 content, the polymer film displays smooth morphology. This indicates that satisfactory interaction takes place between the oxides and the polymer in the presence of the salt. Differential scanning calorimetry (DSC) results corroborate the SEM micrographs, where the crystallinity decreases further to 10% when compared with a pure PEO/Li salt polymer electrolyte. 7Li magic angle spinning (MAS) NMR spectra suggest two major lithium species attributed to the Li+ ions associated with amorphous PEO and Sm2O3. The conductivity in the composite electrolyte is one order of magnitude higher compared with pure PEO/Li electrolyte. The oxide-salt complex functions as cross-linking centres for the PEO segments and establishes additional pathways to conduct ions through the filler surface, thus complements ion movement. The ionic conductivity decreases, with increasing content of Sm2O3 to over 10 wt.% where an aggregated Sm2O3:Li-rich domain is identified.

原文???core.languages.en_GB???
頁(從 - 到)288-294
頁數7
期刊Journal of Power Sources
115
發行號2
DOIs
出版狀態已出版 - 10 4月 2003

指紋

深入研究「Sm2O3 composite PEO solid polymer electrolyte」主題。共同形成了獨特的指紋。

引用此