Single-crystalline Ge nanowires and Cu 3Ge/Ge nano-heterostructures

Shan Chun Hsu, Cheng Lun Hsin, Chun Wei Huang, Shih Ying Yu, Chun Wen Wang, Chi Ming Lu, Kuo Chang Lu, Wen Wei Wu

研究成果: 雜誌貢獻期刊論文同行評審

12 引文 斯高帕斯(Scopus)


Single-crystalline germanium nanowires were synthesized via vapor-liquid-solid mechanism. The characteristics of the Ge nanowires were investigated by a transmission electron microscope to identify the [111] growth direction. The Ge nanowire-based field-effect-transistors on Si 3N 4 dielectrics were fabricated, showing a p-type semiconducting behavior with hole mobility of 47.03 cm 2 V -1 s -1. The formation of Cu 3Ge/Ge/Cu 3Ge nanoheterostructures was demonstrated with the reaction between copper contacts and Ge nanowires by rapid thermal annealing. The diameter-dependent electrical transport property of Ge nanowires indicates that with diameters of more than 80 nm, the resistivity of Ge nanowires decreased with diameter decrease, while with diameters of less than 80 nm, it increased. With multiple annealing processes, the channel length of the Ge nanowire transistors can be successfully controlled. From electrical measurements of each annealing step, the electrical transport property was significantly improved by sequential formation of Cu 3Ge contacts. The gradual formation of the germanide structure reduces Fermi level pinning effect and increases the Ohmic behavior of electrical transportation.

頁(從 - 到)4570-4574
出版狀態已出版 - 21 7月 2012


深入研究「Single-crystalline Ge nanowires and Cu 3Ge/Ge nano-heterostructures」主題。共同形成了獨特的指紋。