Rapid synthesis of MFI zeolite nanocrystals

Cheng Ye Hsu, Anthony S.T. Chiang, Rosilda Selvin, Robert W. Thompson

研究成果: 雜誌貢獻期刊論文同行評審

101 引文 斯高帕斯(Scopus)

摘要

A rapid synthesis procedure for nonagglomerated silicalite nanocrystals has been developed. This was achieved by concentrating the precursor sol before 10-12 h of aging at 80 °C, followed by hydrothermal synthesis at 175 °C for 90 min. The high silica concentration in the concentrated sol accelerated the aggregation of primary units that were present early in the system. Thus, little silica nutrients were left for growth when the secondary particles were converted to zeolite during hydrothermal reaction. As a result, fully dispersible nanocrystals were obtained within a day instead of weeks as reported previously. The aggregation of primary units during the 80 °C aging process as well as the conversion of these aggregates into zeolite has been followed by DLS, XRD, and FTIR. In light of the new results, the nucleation and growth mechanisms of MFI zeolite that have been under debate in the literature were reexamined.

原文???core.languages.en_GB???
頁(從 - 到)18804-18814
頁數11
期刊Journal of Physical Chemistry B
109
發行號40
DOIs
出版狀態已出版 - 13 10月 2005

指紋

深入研究「Rapid synthesis of MFI zeolite nanocrystals」主題。共同形成了獨特的指紋。

引用此