Preparation of TiO2‒B2O3 coating by the sol-gel method

Chih Wen Hsieh, Anthony S.T. Chiang, Cheng Chung Lee, Sheng Jenn Yang

研究成果: 雜誌貢獻期刊論文同行評審

15 引文 斯高帕斯(Scopus)

摘要

Mixed sol of TiO2{single bond}B2O3 was prepared from titanium sec-butoxide and boric acid. This sol could be aged into a clear gel, or dip coated into a transparent film. X-ray diffraction studies on the dried gel show that the transformation from anatase to rutile structure began below 500°C. This temperature is less than the case of pure TiO2. Based on Fourier transform infrared spectra, it is suggested that, after annealing, most boron is in orthoborate groups, the amount of which increases with increasing annealing temperature. The addition of B2O3 also changed the refractive index of the film produced by dip coating, and increased its transmittance in the wavelength range below 550 nm. In addition, it increased the alkaline and acid resistance of the film. Unlike the sol prepared from boron alkoxide, the sol prepared from boric acid was less affected by the atmospheric humidity during the coating process.

原文???core.languages.en_GB???
頁(從 - 到)53-62
頁數10
期刊Journal of Non-Crystalline Solids
144
發行號C
DOIs
出版狀態已出版 - 1992

指紋

深入研究「Preparation of TiO2‒B2O3 coating by the sol-gel method」主題。共同形成了獨特的指紋。

引用此