Polymorphism and phase transitions upon annealing in solvent-cast vs quenched syndiotactic polystyrene and its blends with atactic polystyren

Ya Sen Sun, E. M. Woo, Ming Chien Wu, Rong Ming Ho

研究成果: 雜誌貢獻期刊論文同行評審

17 引文 斯高帕斯(Scopus)

摘要

The crystal polymorphism and phase transition mechanisms upon specific annealing schemes imposed on either neat syndiotactic polystyrene (sPS) or its miscible blends with atactic polystyrene (aPS) were examined using Fourier transform infrared (FT-IR) and wide-angle X-ray diffraction (WAXD). The neat sPS or blends were made in such ways that they started as either initially an amorphous/quenched material or solvent-treated to contain initially some trace crystalline γ-form. Cold crystallization imposed on the initially quenched/amorphous sPS led to the random-coil chains being crystallized into initially a mesomorphic form and subsequently into a more perfect crystalline α-form. IR spectroscopy characterization confirmed a series of structural changes with respect to the annealing temperature imposed on initially quenched/amorphous sPS and revealed a transition from a mesomorphic form to a crystalline α′-form via a nucleation and growth process. Conversely, cold crystallization imposed on the initially quenched miscible blends (sPS/aPS) did not involve a mesomorphic form but developed directly into a crystalline α- and/or β-form upon further annealing to higher temperatures. However, the transition behavior was similar between the solvent-cast neat sPS and solvent-cast sPS/aPS blend upon annealing to higher temperatures. The solvent (1,1,2,2-tetrachloroethane)-induced γ-form in the sPS/aPS blend or neat sPS samples, upon heating to temperatures above 200°C, both exhibited crystal reorganization of the melted crystalline γ-form originally present, which led to formation of the crystalline α′-form. The mechanisms and causes for the different routes of phase transitions in neat sPS or its miscible blends were discussed and analyzed.

原文???core.languages.en_GB???
頁(從 - 到)8415-8425
頁數11
期刊Macromolecules
36
發行號22
DOIs
出版狀態已出版 - 4 11月 2003

指紋

深入研究「Polymorphism and phase transitions upon annealing in solvent-cast vs quenched syndiotactic polystyrene and its blends with atactic polystyren」主題。共同形成了獨特的指紋。

引用此