Modification of silicone elastomer with zwitterionic silane for durable antifouling properties

Shiou Bang Yeh, Chien Sheng Chen, Wen Yih Chen, Chun Jen Huang

研究成果: 雜誌貢獻期刊論文同行評審

112 引文 斯高帕斯(Scopus)

摘要

Biofouling on medical devices generally causes adverse complications, such as thrombosis, infection, and pathogenic calcification. Silicone is a widely used material for medical applications. Its surface modification typically encounters undesirable "hydrophobic recovery", leading to deterioration of surface engineering. In this study, we developed a stable superhydrophilic zwitterionic interface on polydimethylsiloxane (PDMS) elastomer by covalent silanization of sulfobetaine silane (SBSi) to resist nonspecific adsorption of bacteria, proteins, and lipids. SBSi is a zwitterionic organosilane assembly, enabling resisting surface reconstruction by forming a cross-linked network and polar segregation. Surface elemental composition was confirmed by X-ray photoelectron spectroscopy (XPS), and the long-term stability of modification was accessed using a contact angle goniometer. The biofouling tests were carried out by exposing substrates to bacterial, protein, and lipid solutions, revealing the excellent bioinertness of SBSi-tailored PDMS, even after 30 day storage in ambient. For the real-world application, we modified commercially available silicone hydrogel contact lenses with developed zwitterionic silane, presenting its antibacterial adhesion property. Moreover, the cytotoxicity of SBSi was accessed with NIH-3T3 fibroblast by the MTT assay, showing negligible cytotoxicity up to a concentration of 5 mM. Consequently, the strategy of surface engineering in this work can effectively retard the "hydrophobic recovery" occurrence and can be applied to other silicone-based medical devices in a facile way.

原文???core.languages.en_GB???
頁(從 - 到)11386-11393
頁數8
期刊Langmuir
30
發行號38
DOIs
出版狀態已出版 - 30 9月 2014

指紋

深入研究「Modification of silicone elastomer with zwitterionic silane for durable antifouling properties」主題。共同形成了獨特的指紋。

引用此