Mg-Y-Cu bulk nanocrystalline matrix composites containing WC particles

P. Y. Lee, C. Lo, J. S.C. Jang, J. C. Huang

研究成果: 雜誌貢獻期刊論文同行評審

8 引文 斯高帕斯(Scopus)


The preparation of Mg49Y15Cu36 metallic glass composite powders was accomplished by mechanical alloying of pure Mg, Y, Cu, and WC powder mixture after 10 h milling. In the ball-milled composites, initial WC particles were homogeneously dispersed in the Mg-based alloy glassy matrix. The metallic glass composites powders were found to exhibit a large supercooled liquid region before crystallization. Bulk metallic glass composites were formed by vacuum hot pressing the as-milled WC/ Mg49Y 15Cu36 metallic glass composite powders at 473 K in the pressure range of 0.72-1.20 GPa. BMG composite with submicron WC particles homogeneously embedded in a highly dense nanocrystalline/amorphous matrix was successfully prepared under pressure of 1.20 GPa. It was found that the applied pressure during consolidation could enhance the thermal stability and promotes nanocrystallization of WC/Mg49Y15Cu36BMG composites.

頁(從 - 到)25-30
期刊Key Engineering Materials
出版狀態已出版 - 2006


深入研究「Mg-Y-Cu bulk nanocrystalline matrix composites containing WC particles」主題。共同形成了獨特的指紋。