Mechanical properties and fatigue behavior of cast/forged Al1.2%Mg1.0%Si1.0%Cu aluminum alloys

Teng Shih Shih; Jia Wey Lin

doi:10.2320/matertrans.M2018054

Mechanical properties and fatigue behavior of cast/forged Al1.2%Mg1.0%Si1.0%Cu aluminum alloys

Teng Shih Shih, Jia Wey Lin

機械工程學系

研究成果: 雜誌貢獻 › 期刊論文 › 同行評審

1 引文斯高帕斯（Scopus）

摘要

Alloy samples were prepared from Y-block castings. After homogenization treatment, the block samples were held at 195 K, forged using a set of open dies, and then subjected to T6 heat treatment. The tensile specimens were tested to obtain UTS of 420 MPa and an elongation of 12%. After high-cycle fatigue testing, the bare sample exhibited fatigue strength of 117 MPa at 1

原文	???core.languages.en_GB???
頁（從 - 到）	1130-1134
頁數	5
期刊	Materials Transactions
卷	59
發行號	7
DOIs	https://doi.org/10.2320/matertrans.M2018054
出版狀態	已出版 - 2018

存取文件

10.2320/matertrans.M2018054

引用此

@article{591abbd8ea134b299455d4b76868f512,

title = "Mechanical properties and fatigue behavior of cast/forged Al1.2%Mg1.0%Si1.0%Cu aluminum alloys",

abstract = "Alloy samples were prepared from Y-block castings. After homogenization treatment, the block samples were held at 195 K, forged using a set of open dies, and then subjected to T6 heat treatment. The tensile specimens were tested to obtain UTS of 420 MPa and an elongation of 12%. After high-cycle fatigue testing, the bare sample exhibited fatigue strength of 117 MPa at 1",

keywords = "Cast/forged aluminum alloy, Crack initiation, Fatigue life",

author = "Shih, {Teng Shih} and Lin, {Jia Wey}",

note = "Publisher Copyright: {\textcopyright} 2018 The Japan Institute of Metals and Materials.",

year = "2018",

doi = "10.2320/matertrans.M2018054",

language = "???core.languages.en_GB???",

volume = "59",

pages = "1130--1134",

journal = "Materials Transactions",

issn = "1345-9678",

number = "7",

}

TY - JOUR

T1 - Mechanical properties and fatigue behavior of cast/forged Al1.2%Mg1.0%Si1.0%Cu aluminum alloys

AU - Shih, Teng Shih

AU - Lin, Jia Wey

PY - 2018

Y1 - 2018

N2 - Alloy samples were prepared from Y-block castings. After homogenization treatment, the block samples were held at 195 K, forged using a set of open dies, and then subjected to T6 heat treatment. The tensile specimens were tested to obtain UTS of 420 MPa and an elongation of 12%. After high-cycle fatigue testing, the bare sample exhibited fatigue strength of 117 MPa at 1

AB - Alloy samples were prepared from Y-block castings. After homogenization treatment, the block samples were held at 195 K, forged using a set of open dies, and then subjected to T6 heat treatment. The tensile specimens were tested to obtain UTS of 420 MPa and an elongation of 12%. After high-cycle fatigue testing, the bare sample exhibited fatigue strength of 117 MPa at 1

KW - Cast/forged aluminum alloy

KW - Crack initiation

KW - Fatigue life

UR - http://www.scopus.com/inward/record.url?scp=85049165518&partnerID=8YFLogxK

U2 - 10.2320/matertrans.M2018054

DO - 10.2320/matertrans.M2018054

M3 - 期刊論文

AN - SCOPUS:85049165518

SN - 1345-9678

VL - 59

SP - 1130

EP - 1134

JO - Materials Transactions

JF - Materials Transactions

IS - 7

ER -

Mechanical properties and fatigue behavior of cast/forged Al1.2%Mg1.0%Si1.0%Cu aluminum alloys

摘要

存取文件

指紋

引用此