Large-area few-layer MoS2 deposited by sputtering

Jyun Hong Huang, Hsing Hung Chen, Pang Shiuan Liu, Li Syuan Lu, Chien Ting Wu, Cheng Tung Chou, Yao Jen Lee, Lain Jong Li, Wen Hao Chang, Tuo Hung Hou

研究成果: 雜誌貢獻期刊論文同行評審

44 引文 斯高帕斯(Scopus)

摘要

Direct magnetron sputtering of transition metal dichalcogenide targets is proposed as a new approach for depositing large-area two-dimensional layered materials. Bilayer to few-layer MoS2 deposited by magnetron sputtering followed by post-deposition annealing shows superior area scalability over 20 cm2 and layer-by-layer controllability. High crystallinity of layered MoS2 was confirmed by Raman, photo-luminescence, and transmission electron microscopy analysis. The sputtering temperature and annealing ambience were found to play an important role in the film quality. The top-gate field-effect transistor by using the layered MoS2 channel shows typical n-type characteristics with a current on/off ratio of approximately 104. The relatively low mobility is attributed to the small grain size of 0.1-1m with a trap charge density in grain boundaries of the order of 1013 cm-2.

原文???core.languages.en_GB???
文章編號065007
期刊Materials Research Express
3
發行號6
DOIs
出版狀態已出版 - 6月 2016

指紋

深入研究「Large-area few-layer MoS2 deposited by sputtering」主題。共同形成了獨特的指紋。

引用此