Hydrogen embrittlement of AISI 4130 steel with an alternate ferrite/pearlite banded structure

H. L. Lee, S. L.I. Chan

研究成果: 雜誌貢獻期刊論文同行評審

12 引文 斯高帕斯(Scopus)

摘要

The effects of anisotropy on the hydrogen occlusivity, diffusivity and stepwise cracking of AISI 4130 steel with a banded ferrite/pearlite structure were studied. To determine the hydrogen occlusivity with respect to the direction of banding, hydrogen charging in a H "SUB 2" S saturated saline solution was performed. After the specimens had been charged for 2 h, when they were sampled in the longitudinal direction they occluded more hydrogen than when sampled from other directions. When the specimens were sampled in the through-face direction (i.e. with the banding perpendicular to the direction of hydrogen entry), they occluded significantly less hydrogen than in the longitudinal and transverse directions. However, their hydrogen contents reached the same saturation level when the charging period was extended to 8 h. Electrochemical permeation experiments indicate that the effective hydrogen diffusivity along the through-face direction was nearly an order less than that along the other two directions. The effective hydrogen diffusivities of the specimens sectioned in the longitudinal and transverse directions were similar, but the hydrogen permeabilities were different. The results show that the permeation flux of hydrogen along the longitudinal direction was higher than that along the transverse direction. With regard to the susceptibility to hydrogen-induced stepwise cracking, the transverse-sectioned specimens suffered the largest amount of cracking, and the through-face specimens were the most resistant to hydrogen-induced cracking. (A)

原文???core.languages.en_GB???
頁(從 - 到)193-201
頁數9
期刊[No source information available]
142
發行號2
出版狀態已出版 - 1991

指紋

深入研究「Hydrogen embrittlement of AISI 4130 steel with an alternate ferrite/pearlite banded structure」主題。共同形成了獨特的指紋。

引用此