Hot workability of the Mg65Cu20Y10Ag5 amorphous/ nanoZrO2 composite alloy within supercooled temperature region

L. J. Chang, G. R. Fang, J. S.C. Jang, I. S. Lee, J. C. Huang, Chi Y.A. Tsao

研究成果: 雜誌貢獻期刊論文同行評審

1 引文 斯高帕斯(Scopus)

摘要

Mg65Cu20Y10Ag5 Amorphous/ nano ZrO2 composites alloy powder were fabricated through the combination method of melt spinning and mechanical alloying (MA). The melt spun amorphous matrix ribbons are ground into powders and mixed with 3 vol.% ZrO2 nano particles in the planetary mill. After then formed by hot pressing in Ar atmosphere under the pressure of 700 MPa at the temperature of soft point which measured by TMA (Thermal mechanical Analysis). The hot-pressed bulk composite specimens are compression tested at different temperature within the supercooled temperature region. The flow stress was found decrease with increasing temperature dramatically when the temperature exceeds the middle temperature of supercooled region. The specimens after compression test were examined by X-ray diffractometry and SEM to investigate its crystallinity and fracture mechanism.

原文???core.languages.en_GB???
頁(從 - 到)103-108
頁數6
期刊Key Engineering Materials
351
DOIs
出版狀態已出版 - 2007

指紋

深入研究「Hot workability of the Mg65Cu20Y10Ag5 amorphous/ nanoZrO2 composite alloy within supercooled temperature region」主題。共同形成了獨特的指紋。

引用此