Heterogenization of organometallic molybdenum complexes with siloxane functional groups and their catalytic application

Ayyamperumal Sakthivel, Jin Zhao, Marianne Hanzlik, Anthony S.T. Chiang, Wolfgang A. Herrmann, Fritz E. K̈uhn

研究成果: 雜誌貢獻期刊論文同行評審

77 引文 斯高帕斯(Scopus)

摘要

η5-CpMo(CO)3R complexes containing siloxane functional groups [(CH2)3Si(OMe)3 or (CH 2) Si(OEt)3] attached to either the cyclopentadiene ligand or directly to Mo were grafted on the mesoporous materials MCM-41 and MCM-48 by reaction of the OR (R = Me, Et) moieties in the silane ligand and surface silanol groups (Si-OH). For the sake of comparison mesoporous materials modified with silane groups were reacted with Na+[CpMo(CO)3] -. The XRD, N2 adsorption-desorption, and TEM analyses provide strong evidence that the mesoporous structure of the supporting material retains its long-range ordering throughout the grafting process, despite significant reductions in surface area, pore volume and pore size. The appearance of strong IR bands around 2016 and 1956 cm-1 on the grafted samples also shows that the η5- ÏñÌï(ÏÏ)3Ê complexes have been successfully grafted. Elemental analysis reveals that the grafted samples contain 0.3-3.5 wt % Mo. 29Si CP MAS-NMR spectra give clear evidence for a reduction in the numbers of the Q3 and Q2 sites. The formation of new peaks around -49.8, -57.9, and -66.2 ppm (T1, T2, and T3) indicates esterification of silanol groups by the alkoxy groups of the silane ligand. Both the in situ and ex situ prepared samples show good catalytic activity for the epoxidation of cyclooctene.

原文???core.languages.en_GB???
頁(從 - 到)473-483
頁數11
期刊Advanced Synthesis and Catalysis
347
發行號2-3
DOIs
出版狀態已出版 - 2月 2005

指紋

深入研究「Heterogenization of organometallic molybdenum complexes with siloxane functional groups and their catalytic application」主題。共同形成了獨特的指紋。

引用此