Growth of InSb and InAs1-xSbx on GaAs by molecular beam epitaxy

J. I. Chyi, S. Kalem, N. S. Kumar, C. W. Litton, H. Morkoç

研究成果: 雜誌貢獻期刊論文同行評審

98 引文 斯高帕斯(Scopus)

摘要

InSb and InAs1-xSbx epitaxial layers have been successfully grown on (100)GaAs substrates by molecular beam epitaxy. Remarkably good morphologies were obtained despite the large lattice mismatch (14%) between InSb and GaAs. Room-temperature electron mobilities as high as 57 000 cm2/V s were measured in InSb layers of about 5 μm thick with ND-NA∼1.6×1016 cm-3. The substrate temperature and Sb/In flux ratio were found to critically influence the quality of InSb epilayers. By employing dimeric instead of tetrameric sources, the composition of the InAs1-xSbx films was observed to be relatively independent of substrate temperature. Electron mobilities of 20 000 and 8800 cm2/V s, at 300 and 77 K, respectively, were obtained for a 1.6-μm-thick InAs1-xSbx (x=0.67) layer.

原文???core.languages.en_GB???
頁(從 - 到)1092-1094
頁數3
期刊Applied Physics Letters
53
發行號12
DOIs
出版狀態已出版 - 1988

指紋

深入研究「Growth of InSb and InAs1-xSbx on GaAs by molecular beam epitaxy」主題。共同形成了獨特的指紋。

引用此