Gas permeability and stability of poly(1‐trimethylsilyl‐1‐propyne‐co‐1‐phenyl‐1‐propyne) membranes

Kazukiyo Nagai, Akon Higuchi, Tsutomu Nakagawa

研究成果: 雜誌貢獻期刊論文同行評審

111 引文 斯高帕斯(Scopus)

摘要

A significant reduction in the gas permeability of the poly(1‐trimethylsilyl‐1‐propyne) (PMSP) membrane was investigated in terms of the membrane thickness and the storage environment. The effects of physical aging were observed with thinner membranes and under vacuum conditions compared with storage in air. The decrease in the permeability coefficient was dependent on the decrease in the hole saturation constant of Langmuir adsorption (C'H), which is related to the volume of the microvoids. Physical aging in the PMSP membrane affected not only the glassy domain but also the rubbery one. To stabilize the permeability of the PMSP membrane, a poly(1‐trimethylsilyl‐1‐propyne‐co‐1‐phenyl‐1‐propyne) [poly(TMSP‐co‐PP)] membrane was prepared. Poly(TMSP‐co‐PP) has the same unit of poly(1‐phenyl‐1‐propyne), which membrane has stable permeability. The poly(TMSP‐co‐PP) with less than 20 mol % PP content was estimated to be a random copolymer based on theoretical gas permeation analysis. In the poly(TMSP‐co‐PP) membrane, the relation between the PP content and C'H was similar to the relation between the PP content and the gas permeability. The stability of the permeability was dependent on the PP content. The poly(TMSP‐co‐PP) membrane containing 10 mol % PP had both high permeability and good stability under some of the aging conditions performed in this work. © 1995 John Wiley & Sons, Inc.

原文???core.languages.en_GB???
頁(從 - 到)289-298
頁數10
期刊Journal of Polymer Science, Part B: Polymer Physics
33
發行號2
DOIs
出版狀態已出版 - 30 1月 1995

指紋

深入研究「Gas permeability and stability of poly(1‐trimethylsilyl‐1‐propyne‐co‐1‐phenyl‐1‐propyne) membranes」主題。共同形成了獨特的指紋。

引用此