Fatigue properties improvement of high-strength aluminum alloy by using a ZrCu-based metallic glass thin film coating

P. H. Tsai, J. B. Li, Y. Z. Chang, H. C. Lin, J. S.C. Jang, J. P. Chu, J. W. Lee, P. K. Liaw

研究成果: 雜誌貢獻期刊論文同行評審

16 引文 斯高帕斯(Scopus)

摘要

For further enhancing the fatigue properties of high-strength aluminum alloy, the coating, which was combined with a layer of 200 nm ZrCu-based metallic glass thin film (MGTF) coupled with 50 nm titanium thin film buffer layer, was applied to coat on the surface of 7075-T6 aluminum alloy by the DC sputtering method. The results show that the fatigue limit could be significantly improved from 150 MPa for the uncoated sample to 250 MPa (66.7% increase) for the samples coated with ZrCu-based MGTF. In parallel, the fatigue life of 7075-T6 aluminum alloy with ZrCu-based MGTF could be drastically improved 45 times at a stress level of 250 MPa than the bare one. The outstanding mechanical properties of ZrCu-based MGTF, such as high strength and good adhesion between the film and the substrate, are the key factors to enhance the fatigue resistance of the coated aluminum alloy.

原文???core.languages.en_GB???
頁(從 - 到)28-32
頁數5
期刊Thin Solid Films
561
DOIs
出版狀態已出版 - 30 6月 2014

指紋

深入研究「Fatigue properties improvement of high-strength aluminum alloy by using a ZrCu-based metallic glass thin film coating」主題。共同形成了獨特的指紋。

引用此