Fatigue of as-extruded AZ61A magnesium alloy

Teng Shih Shih, Wen Sun Liu, Yeong Jern Chen

研究成果: 雜誌貢獻期刊論文同行評審

129 引文 斯高帕斯(Scopus)

摘要

Samples prepared from as-extruded AZ61A bars (18 mm in diameter) were used in a rotating bending test. The relation between stress amplitude and cycles to failure has been constructed, as well as the cycles to failure at two specific stress amplitudes. The probability of failure at these two specific stress levels was also analyzed. This study finally provided the predicted fatigue strength at 107 cycles with different probabilities (10 to 90%). A fractography study indicated that fatigue cracking initiated from subsurface or surface inclusions. These inclusions near the surface served as stress raisers and induced clusters of slip bands during the rotating bending test. After initiation, the cracks grew under the dominant shear stress and resulted in a cleavage fracture over a large area. Microscopic cracks occurred, resulting from the induced deformation twins that developed from the blunting process. Consequently, the propagation of cracks followed the existence of microscopic cracks and resulted in a transgranular fracture.

原文???core.languages.en_GB???
頁(從 - 到)152-162
頁數11
期刊Materials Science and Engineering A
325
發行號1-2
DOIs
出版狀態已出版 - 28 2月 2002

指紋

深入研究「Fatigue of as-extruded AZ61A magnesium alloy」主題。共同形成了獨特的指紋。

引用此