Evolution of microstructure of AISI 304 stainless steel joint brazed by mechanically alloyed nickel base filler with different silicon content

J. S.C. Jang, H. P. Shih

研究成果: 雜誌貢獻期刊論文同行評審

21 引文 斯高帕斯(Scopus)

摘要

The evolution of microstructure of AlSI 304 stainless steel joint was studied. The joint was brazed by mechanically alloyed nickel base filler with different silicon content. The microstructures were examined by X ray diffraction and scanning electron microscopy. It was found that when Si content reaches 8.5 wt% and the brazing temperature was increased to 1091 °C, greater interdiffusion occurred between the base metal and the brazing joint.

原文???core.languages.en_GB???
頁(從 - 到)79-82
頁數4
期刊Journal of Materials Science Letters