Electroless Ni-P/diamond /graphene composite coatings and characterization of their wear and corrosion resistance in sodium chloride solution

Cheng Kuo Lee, Chi Lun Teng, An Hung Tan, Ching Yi Yang, Sheng Long Lee

研究成果: 書貢獻/報告類型會議論文篇章同行評審

6 引文 斯高帕斯(Scopus)

摘要

The purpose of the present study is to evaluate the effect of the electroless Ni-P/diamond/graphene composite coating on the structure and surface hardness of 2024-T6 aluminum alloy as well as their effect on the corrosion and wear resistance of the alloy in 3.5 % NaCl solution. The electroless Ni-P plating solution was prepared by adding different size diamond (6-12 μm and 0.2 μm) and nano-graphene into the electroless Ni-P plating solution to obtain Ni-P/diamond, Ni-P/graphene and Ni-P/daimond/graphene composite coatings for comparison. Experimental results indicated that the Ni-P/diamond, Ni-P/graphene and Ni-P/daimond/graphene composite coatings can be successfully electroless deposited on anodized 2024-T6 aluminum alloy. The anodically oxidized films, that formed on the aluminum alloy using phosphoric acid as the electrolyte, was porous with high density of pores, and thus could enhance the adhesion of the composite coatings. The Ni-P/daimond/graphene hybrid coating had a higher hardness as well as better corrosion and wear resistance of 2024-T6 alloy in 3.5 wt.% NaCl solution as compared with other composite coatings. When the combination of nano-graphene and smaller diamond particles added this beneficial effect was significantly raised, especially the composite coating was further vacuum annealed at 400°C for 24 h to obtain a more smooth and defect-free coating structure.

原文???core.languages.en_GB???
主出版物標題Recent Development in Machining, Materials and Mechanical Technologies
編輯Jyh-Chen Chen, Usuki Hiroshi, Sheng-Wei Lee, Yiin-Kuen Fuh
發行者Trans Tech Publications Ltd
頁面51-56
頁數6
ISBN(列印)9783038354956
DOIs
出版狀態已出版 - 2015
事件International Conference on Machining, Materials and Mechanical Technologies, IC3MT 2014 - Taipei City, Taiwan
持續時間: 31 8月 20145 9月 2014

出版系列

名字Key Engineering Materials
656-657
ISSN(列印)1013-9826
ISSN(電子)1662-9795

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???International Conference on Machining, Materials and Mechanical Technologies, IC3MT 2014
國家/地區Taiwan
城市Taipei City
期間31/08/145/09/14

指紋

深入研究「Electroless Ni-P/diamond /graphene composite coatings and characterization of their wear and corrosion resistance in sodium chloride solution」主題。共同形成了獨特的指紋。

引用此