Electrochemical behavior of anodized AA6063-T6 alloys affected by matrix structures

Yung Sen Huang, Teng Shih Shih, Chen En Wu

研究成果: 雜誌貢獻期刊論文同行評審

17 引文 斯高帕斯(Scopus)

摘要

AA 6063 alloys were cold-rolled (CR) either before or after solution treatment (S) and then different samples were artificially aged (T6) to obtain different samples (CRST6 and SCRT6). The highest dislocation density was observed in the SCRT6 sample which also showed the lowest particle count among the three samples; ST6, CRST6 and SCRT6. Subsequently, all samples were anodized in a 15 wt% sulfuric acid solution for different time spans to obtain anodic aluminum oxide (AAO) films. The anodized samples were further analyzed with X-ray Photoelectron Spectroscopy (XPS) analysis. We determined that the constituent phases in the AAO film were composed of hydrated amorphous alumina, hydrated oxide (Al(OH) 3 ) and oxyhydroxide (AlOOH) phases together with some silicon-containing particles trapped in the films on all samples. In the electrochemical test, the silicon-containing particles and hydrated Al(OH) 3 oxide that existed at the electrolyte/film (e/f) interface were found to inversely influence the corrosion resistance of the anodized samples.

原文???core.languages.en_GB???
頁(從 - 到)410-418
頁數9
期刊Applied Surface Science
264
DOIs
出版狀態已出版 - 1 1月 2013

指紋

深入研究「Electrochemical behavior of anodized AA6063-T6 alloys affected by matrix structures」主題。共同形成了獨特的指紋。

引用此