Electro-chromic device with GZO as a conductive layer

Chih Chao Chan, Chien Jen Tang, Kun Hsien Lee, Cheng Chung Jaing, Chien Cheng Kuo, Hsi Chao Chen, Cheng Chung Lee

研究成果: 書貢獻/報告類型會議論文篇章同行評審

1 引文 斯高帕斯(Scopus)

摘要

Thin films of tungsten oxide (WO3) were deposited on GZO-coated B270 glass substrates and thin films of Ta2O5 were deposited on B270 glass substrates by electron beam gun evaporation at high vacuum pressure of 3×10-5 Torr and varied oxygen pressures ranging from 1.0×10-4 to 6.0×10-4 Torr. The optical properties of the electro-chromic (EC) film were measured by a spectrophotometer. The optical modulation (ΔT) of the tungsten oxide thin film deposited at an oxygen pressure of 1.0×10-4 Torr was found to be ΔT = 67.46% at λ=550nm. The optimum optical properties for deposition of Ta2O5 were attained at an oxygen pressure of 4x10-4 Torr. Gallium doped zinc oxide (GZO) was used as a conductive layer instead of ITO. A five layer EC device (Glass/GZO/WO3/Ta 2O5/NiO/Al) has been design and fabricated.

原文???core.languages.en_GB???
主出版物標題Current Developments in Lens Design and Optical Engineering XI; and Advances in Thin Film Coatings VI
DOIs
出版狀態已出版 - 2010
事件Current Developments in Lens Design and Optical Engineering XI; and Advances in Thin Film Coatings VI - San Diego, CA, United States
持續時間: 1 8月 20103 8月 2010

出版系列

名字Proceedings of SPIE - The International Society for Optical Engineering
7786
ISSN(列印)0277-786X

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???Current Developments in Lens Design and Optical Engineering XI; and Advances in Thin Film Coatings VI
國家/地區United States
城市San Diego, CA
期間1/08/103/08/10

指紋

深入研究「Electro-chromic device with GZO as a conductive layer」主題。共同形成了獨特的指紋。

引用此