Effects of Cryogenic Forging and Anodization on the Mechanical Properties of AA 7075-T73 Aluminum Alloys

Teng Shih Shih; Tien Wei Liao; Wen Nong Hsu

doi:10.1007/s11665-016-1946-2

Effects of Cryogenic Forging and Anodization on the Mechanical Properties of AA 7075-T73 Aluminum Alloys

Teng Shih Shih, Tien Wei Liao, Wen Nong Hsu

機械工程學系

研究成果: 雜誌貢獻 › 期刊論文 › 同行評審

3 引文斯高帕斯（Scopus）

摘要

In this study, high-strength AA7075 alloy samples were cryogenically forged after annealing and then subjected to solution and aging treatments. The cryogenically forged 7075-T73 alloy samples displayed equiaxed fine grains associated with abundant fine precipitates in their matrix. Compared with conventional 7075-T73 alloy samples, the cryogenically forged samples exhibited an 8-12% reduction in tensile strength and an increased fatigue strength and higher corrosion resistance. The fatigue strength measured at 10⁷ cycles was 225 MPa in the bare samples; the strength was increased to 250 MPa in the cryogenically forged samples. The effect of anodization on the corrosion resistance of the bare samples was improved from (E_corr) −0.80 to −0.61 V.

原文	???core.languages.en_GB???
頁（從 - 到）	1211-1218
頁數	8
期刊	Journal of Materials Engineering and Performance
卷	25
發行號	3
DOIs	https://doi.org/10.1007/s11665-016-1946-2
出版狀態	已出版 - 1 3月 2016

存取文件

10.1007/s11665-016-1946-2

引用此

@article{d00e8b19c9c54db8b3b1855b8fa1ae5e,

title = "Effects of Cryogenic Forging and Anodization on the Mechanical Properties of AA 7075-T73 Aluminum Alloys",

abstract = "In this study, high-strength AA7075 alloy samples were cryogenically forged after annealing and then subjected to solution and aging treatments. The cryogenically forged 7075-T73 alloy samples displayed equiaxed fine grains associated with abundant fine precipitates in their matrix. Compared with conventional 7075-T73 alloy samples, the cryogenically forged samples exhibited an 8-12% reduction in tensile strength and an increased fatigue strength and higher corrosion resistance. The fatigue strength measured at 107 cycles was 225 MPa in the bare samples; the strength was increased to 250 MPa in the cryogenically forged samples. The effect of anodization on the corrosion resistance of the bare samples was improved from (Ecorr) −0.80 to −0.61 V.",

keywords = "7075-T73, anodization, cryogenic forging, precipitates",

author = "Shih, {Teng Shih} and Liao, {Tien Wei} and Hsu, {Wen Nong}",

note = "Publisher Copyright: {\textcopyright} 2016, ASM International.",

year = "2016",

month = mar,

day = "1",

doi = "10.1007/s11665-016-1946-2",

language = "???core.languages.en_GB???",

volume = "25",

pages = "1211--1218",

journal = "Journal of Materials Engineering and Performance",

issn = "1059-9495",

number = "3",

}

TY - JOUR

T1 - Effects of Cryogenic Forging and Anodization on the Mechanical Properties of AA 7075-T73 Aluminum Alloys

AU - Shih, Teng Shih

AU - Liao, Tien Wei

AU - Hsu, Wen Nong

PY - 2016/3/1

Y1 - 2016/3/1

N2 - In this study, high-strength AA7075 alloy samples were cryogenically forged after annealing and then subjected to solution and aging treatments. The cryogenically forged 7075-T73 alloy samples displayed equiaxed fine grains associated with abundant fine precipitates in their matrix. Compared with conventional 7075-T73 alloy samples, the cryogenically forged samples exhibited an 8-12% reduction in tensile strength and an increased fatigue strength and higher corrosion resistance. The fatigue strength measured at 107 cycles was 225 MPa in the bare samples; the strength was increased to 250 MPa in the cryogenically forged samples. The effect of anodization on the corrosion resistance of the bare samples was improved from (Ecorr) −0.80 to −0.61 V.

AB - In this study, high-strength AA7075 alloy samples were cryogenically forged after annealing and then subjected to solution and aging treatments. The cryogenically forged 7075-T73 alloy samples displayed equiaxed fine grains associated with abundant fine precipitates in their matrix. Compared with conventional 7075-T73 alloy samples, the cryogenically forged samples exhibited an 8-12% reduction in tensile strength and an increased fatigue strength and higher corrosion resistance. The fatigue strength measured at 107 cycles was 225 MPa in the bare samples; the strength was increased to 250 MPa in the cryogenically forged samples. The effect of anodization on the corrosion resistance of the bare samples was improved from (Ecorr) −0.80 to −0.61 V.

KW - 7075-T73

KW - anodization

KW - cryogenic forging

KW - precipitates

UR - http://www.scopus.com/inward/record.url?scp=84961156618&partnerID=8YFLogxK

U2 - 10.1007/s11665-016-1946-2

DO - 10.1007/s11665-016-1946-2

M3 - 期刊論文

AN - SCOPUS:84961156618

SN - 1059-9495

VL - 25

SP - 1211

EP - 1218

JO - Journal of Materials Engineering and Performance

JF - Journal of Materials Engineering and Performance

IS - 3

ER -

Effects of Cryogenic Forging and Anodization on the Mechanical Properties of AA 7075-T73 Aluminum Alloys

摘要

存取文件

指紋

引用此