Effect of Cylinder Size on the Compressive Strength of Concrete CO2 Curing

Ming Gin Lee, Yung Chih Wang, Yu Min Su, Yu Cheng Kan, Shih Hsuan Kao

研究成果: 書貢獻/報告類型會議論文篇章同行評審

2 引文 斯高帕斯(Scopus)

摘要

This study was conducted to assess the effect of cylinder size on concrete compressive strength by CO2 curing. The factors studied to evaluate the effect of cylinder size on concrete compressive strength were cylinder size, CO2 concentration, curing pressure, curing time, and age of specimen at testing. Three different cylinder sizes (5 × 10 cm, 10 × 20 cm, 15 × 30 cm), three CO2 concentration (50%, 75%, 100%), three curing time (1, 3, 6 h), three curing pressures (2, 4, 8 bars), and four testing ages (3, 7, 28, 90 days) were used in this investigation. A batch size of 0.18 m3 concrete was used to produce twenty 5 × 10 cm cylinders, twenty 10 × 20 cm cylinders, and twelve 15 × 30 cm cylinders. However, it was necessary that the specimens reach an initial set to demold before the CO2 curing process was used because the dry CO2 gas-stream would gradually take the free water away from the specimens. After the CO2 curing duration, the concrete samples were assessed through the compressive strength, the pressure drop and the temperature expected to go down and rise in the chamber. In general, high early and late compressive strength of the CO2-cured cylinders were obtained while its strength was mostly higher than the strength of normally water-cured ones. The ks5 value obtained from 5 × 10 cm, and 15 × 30 cm cylinders by CO2 curing ranges between 0.95 and 1.30, this is partly due to the fact that high early compressive strength of the CO2-cured cylinders was obtained while its early strength was about equal to the 28-day strength of normally water-cured ones. Therefore, special care is still needed to compare the properties of concrete from the two different cylinder sizes by CO2 curing.

原文???core.languages.en_GB???
主出版物標題Transportation and Geotechniques
主出版物子標題Materials, Sustainability and Climate - Proceedings of the 5th GeoChina International Conference 2018 – Civil Infrastructures Confronting Severe Weathers and Climate Changes: From Failure to Sustainability, 2018 in HangZhou, China
編輯Manik Barman, Musharraf Zaman, Jia-Ruey Chang
發行者Springer Science and Business Media B.V.
頁面33-42
頁數10
ISBN(列印)9783319957678
DOIs
出版狀態已出版 - 2019
事件5th GeoChina International Conference on Civil Infrastructures Confronting Severe Weathers and Climate Changes: From Failure to Sustainability, 2018 - HangZhou, China
持續時間: 23 7月 201825 7月 2018

出版系列

名字Sustainable Civil Infrastructures
ISSN(列印)2366-3405
ISSN(電子)2366-3413

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???5th GeoChina International Conference on Civil Infrastructures Confronting Severe Weathers and Climate Changes: From Failure to Sustainability, 2018
國家/地區China
城市HangZhou
期間23/07/1825/07/18

指紋

深入研究「Effect of Cylinder Size on the Compressive Strength of Concrete CO2 Curing」主題。共同形成了獨特的指紋。

引用此