Effect of Al and Mn content on the mechanical properties of various ECAE processed Mg-Li-Zn alloys

Jian Yih Wang, Tien Chan Chang, Li Zen Chang, Shyong Lee

研究成果: 雜誌貢獻期刊論文同行評審

19 引文 斯高帕斯(Scopus)


The equal channel angular extrusion (ECAE) process is an innovative method to refine grain structure; however, it could be highly technical to perform to result in subsequent exotic mechanical properties. This study will demonstrate how easy or difficult of this operation. Yoshida et al. had applied the ECAE process on Mg-10%Li-1%Zn alloy to obtain a max. superplastic elongation of 421 %. This paper tries to reproduce it with Mg-11%Li-1%Zn and Mg-9%Li-1%Zn alloys via the same ECAE process. For the 28 specimens having received 4 passes of ECAE, one of them shows a comparable but lesser elongation of 350% under selective temperature of 523 K and strain rate, 1 × 10-4 s -1, and the corresponding strain rate sensitivity exponent is 0.48. Furthermore, the ECAE process is imposed on three other Mg-Li-Zn alloys containing Al and Mn (Mg-9%Li-1%Zn-0.2%Mn, Mg-9%Li-1%Zn-1%Al-0.2%Mn and Mg-9%Li-3%Al-1%Zn-0.2%Mn), and this investigation is unprecedented. The original justification for this exploration is that Al and Mn addition may strengthen the α and β phases which are the sole micro-constituents of Mg-Li alloys when bearing Li content between 5% to 11%. Indeed, it is so at room temperature as determined by microhardness testing. However, high temperature tensile elongation is not benefited.

頁(從 - 到)971-976
期刊Materials Transactions
出版狀態已出版 - 4月 2006


深入研究「Effect of Al and Mn content on the mechanical properties of various ECAE processed Mg-Li-Zn alloys」主題。共同形成了獨特的指紋。