Cyclic fatigue of hot isostatically pressed silicon nitride at elevated temperatures

C. K.J. Lin, M. G. Jenkins, M. K. Ferber

研究成果: 雜誌貢獻期刊論文同行評審

22 引文 斯高帕斯(Scopus)

摘要

Cyclic fatigue properties of a hot isostatically pressed silicon nitride were investigated at 1150, 1260 and 1370 °C in ambient air. The uniaxial tensile tests were conducted under various cyclic loading wave forms and frequencies. The correlation of stress-life relations between cyclic and static fatigue results was evaluated. At 1150-1370 °C, cyclic loading caused less damage than static loading, as evidenced by the longer failure time under cyclic loading versus static loading with the same maximum applied stresses. The cyclic loading effect was more pronounced in high frequency tests at 1260 and 1370 °C and might be related to the viscoelastic behaviour of the intergranular phase. Microstructural analyses and macroscopic cyclic stress-strain and strain-time relations indicated that cyclic loading/unloading may inhibit the normal accumulation of creep damage.

原文???core.languages.en_GB???
頁(從 - 到)3517-3526
頁數10
期刊Journal of Materials Science
29
發行號13
DOIs
出版狀態已出版 - 1月 1994

指紋

深入研究「Cyclic fatigue of hot isostatically pressed silicon nitride at elevated temperatures」主題。共同形成了獨特的指紋。

引用此