Cs 3UGe 7O 18: A pentavalent uranium germanate containing four- and six-coordinate germanium

Quang Bac Nguyen, Chun Liang Chen, Yun Wei Chiang, Kwang Hwa Lii

研究成果: 雜誌貢獻期刊論文同行評審

24 引文 斯高帕斯(Scopus)

摘要

A pentavalent uranium germanate, Cs 3UGe 7O 18, was synthesized under high-temperature, high-pressure hydrothermal conditions at 585 °C and 160 MPa and structurally characterized by single-crystal X-ray diffraction and infrared spectroscopy. The valence state of uranium was confirmed by X-ray photoelectron spectroscopy and electron paramagnetic resonance. The room-temperature EPR spectrum can be simulated with two components using an axial model that are consistent with two distinct sites of uranium(V). In the structure of the title compound, each [6]GeO 6 octahedron is bonded to six three-membered single-ring [4]Ge 3O 9 6- units to form germanate triple layers in the ab plane. Each layer contains nine-ring windows; however, these windows are blocked by adjacent layers. The triple layers are further connected by UO 6 octahedra to form a three-dimensional framework with intersecting six-ring channels along the 〈11̄0〉 directions. The Cs + cation sites are fully occupied, ordered, and located in the cavities of the framework. Pentavalent uranium germanates or silicates are very rare, and only two uranium silicates and one germanate analogue have been published. However, all of them are iso-structural with those of the Nb or Ta analogues. In contrast, the title compound adopts a new structural type and contains both four- and six-coordinate germanium. Crystal data of Cs 3UGe 7O 18: trigonal, P3̄c1 (No. 165), a = 12.5582(4) Å, c = 19.7870(6) Å, V = 2702.50(15) Å 3, Z = 6, D calc = 5.283 g•cm -3, μ(Mo Kα) = 26.528 mm -1, R 1 = 0.0204, wR 2 = 0.0519 for 1958 reflections with I > 2σ(I). GooF = 1.040, ρ max,min = 1.018, and -1.823 e•Å -3.

原文???core.languages.en_GB???
頁(從 - 到)3879-3882
頁數4
期刊Inorganic Chemistry
51
發行號6
DOIs
出版狀態已出版 - 19 3月 2012

指紋

深入研究「Cs 3UGe 7O 18: A pentavalent uranium germanate containing four- and six-coordinate germanium」主題。共同形成了獨特的指紋。

引用此