Corrosion fatigue behavior of 7050 aluminum alloys in different tempers

Chih Kuang Lin, Sheno Tseng Yang

研究成果: 雜誌貢獻期刊論文同行評審

64 引文 斯高帕斯(Scopus)

摘要

Corrosion fatigue (CF) experiments, including both high-cycle axial fatigue (S-N curve) and fatigue crack growth (FCG), have been performed on 7050 aluminium alloys in a 3.5 wt% NaCl solution as a function of aging treatment. The results of these environmental tests were compared with those obtained in laboratory air to characterize the effect of aging treatment on CF susceptibility. Fatigue resistance in both peak aged (T6) and overaged (Y73) tempers was dramatically reduced by the aqueous chloride environment. The FCG rates for Y73 condition were lower than the counterparts for T6 condition in both air and saline solution. 7050-T73 alloy exhibited longer fatigue lives in air but shorter ones in the corrosive environment as compared to the T6 temper. This may be attributed to the formation of more extensive and larger corrosion pits acting as crack nuclei to facilitate crack initiation, in the T73 tempered condition. Comparison of CF and stress corrosion cracking (SCC) results reveals that overaging treatments used to improve grain boundary characteristics and increase the intergranular SCC resistance might not guarantee an equivalent improvement in the resistance to transgranular CF cracking.

原文???core.languages.en_GB???
頁(從 - 到)779-795
頁數17
期刊Engineering Fracture Mechanics
59
發行號6
DOIs
出版狀態已出版 - 6 4月 1998

指紋

深入研究「Corrosion fatigue behavior of 7050 aluminum alloys in different tempers」主題。共同形成了獨特的指紋。

引用此