Characterization of polyaniline synthesized from chemical oxidative polymerization at various polymerization temperatures

Ku Yen Lin, Lun Wei Hu, Ko Lun Chen, Ming Deng Siao, Wei Fu Ji, Chun Chuen Yang, Jui Ming Yeh, Kuan Cheng Chiu

研究成果: 雜誌貢獻期刊論文同行評審

14 引文 斯高帕斯(Scopus)

摘要

We report on the effects from polymerization temperature (TP) on the thermal de-protonation of anilinium cations into neutral anilines and on the structural and electrical properties of polyaniline emeraldine salt (PANI ES) samples synthesized from chemical oxidative polymerization with ammonium peroxydisulfate as oxidant and with [HCl] varied from 0.7, 1.0, and 2.0 M. From the TP–dependence of induction period the activation energy associated with this thermal de-protonation is evaluated. With increasing TP to increase the de-protonation rate, the as-synthesized PANI ES samples possess a weaker hardness, a less crystallinity, a lower molecular weight and a smaller dispersity. From the temperature-dependence of electrical conductivity measured on these doped PANI ES samples and with application of the nearest-neighbor hopping model, the corresponding activation energy for charge transport increases with increasing TP. Above results reveal that the distribution of polaron states induced by counter-ions in the PANI ES sample synthesized at higher TP becomes more disorder and hence results in a broader polaron bandwidth.

原文???core.languages.en_GB???
頁(從 - 到)311-319
頁數9
期刊European Polymer Journal
88
DOIs
出版狀態已出版 - 1 3月 2017

指紋

深入研究「Characterization of polyaniline synthesized from chemical oxidative polymerization at various polymerization temperatures」主題。共同形成了獨特的指紋。

引用此