Annealing effect of polymer bulk heterojunction solar cells based on polyfluorene and fullerene blend

Jen Hsien Huang, Chuan Yi Yang, Zhong Yo Ho, Dhananjay Kekuda, Meng Chyi Wu, Fan Ching Chien, Peilin Chen, Chih Wei Chu, Kuo Chuan Ho

研究成果: 雜誌貢獻期刊論文同行評審

91 引文 斯高帕斯(Scopus)

摘要

Control of blend morphology at the nanoscale and high charge mobility is essential for polymer photovoltaic devices in terms of their power conversion efficiencies (PCE). In the case of bulk heterojunctions solar cells, both blend morphology and charge mobility are influenced by thermal treatment. In this manuscript, we study the effects of annealing temperature on polymer PV devices with blends of poly[9,9'- dioctyl-fluorene-co-bithiophene] (F8T2) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM). The morphological changes of blended films were observed upon thermal annealing temperature near and above glass transition temperature (130 °C). Such microstructural transformations resulted in modified charge transport pathways and therefore greately influenced the device performance. The highest PCE of 2.14% with an open-circuit voltage (VOC) of 0.99 V and a short-circuit current (JSC) of 4.24 mA/cm2 was achieved by device annealing at 70 °C for 20 min.

原文???core.languages.en_GB???
頁(從 - 到)27-33
頁數7
期刊Organic Electronics
10
發行號1
DOIs
出版狀態已出版 - 2月 2009

指紋

深入研究「Annealing effect of polymer bulk heterojunction solar cells based on polyfluorene and fullerene blend」主題。共同形成了獨特的指紋。

引用此