A facile and rapid sonochemical route to synthesize highly ordered mesoporous silicas MCM-48 and Al-MCM-48 with Ia3d cubic structure using gemini surfactant

Hao Yiang Wu, Shi Zhe Huang, Chun Chiang Ting, Juti Rani Deka, Hsien Ming Kao

研究成果: 雜誌貢獻期刊論文同行評審

1 引文 斯高帕斯(Scopus)

摘要

Highly ordered cubic mesoporous silicas MCM-48 and Al-MCM-48 with high surface areas were successfully synthesized using Gemini surfactant as template under basic conditions within a very short time period with the aid of ultrasonic irradiation. The introduction of ultrasonic irradiation as an intermediate synthesis step before the hydrothermal treatment has reduced the total synthesis time significantly from 7 days to 24 hours, which is much shorter than the required time for the conventional synthesis of MCM-48 directly via the hydrothermal route alone. The structural and textural properties of the resultant materials can be finely tuned by varying the ultrasonic irradiation time for pure MCM-48 and Al-MCM-48 with various Si/Al ratios. The final products exhibited well ordered cubic Ia3d mesostructure with surface areas in the range of 968-1861 m2g-1, pore volumes of 0.52-0.91 cm 3g-1, and pore diameters in the range of 1.9-2.9 nm, which are comparable to the conventional analogues.

原文???core.languages.en_GB???
頁(從 - 到)831-838
頁數8
期刊Journal of the Chinese Chemical Society
60
發行號7
DOIs
出版狀態已出版 - 7月 2013

指紋

深入研究「A facile and rapid sonochemical route to synthesize highly ordered mesoporous silicas MCM-48 and Al-MCM-48 with Ia3d cubic structure using gemini surfactant」主題。共同形成了獨特的指紋。

引用此