Study of LiFePO4 cathode materials coated with high surface area carbon

Cheng Zhang Lu, George Ting Kuo Fey, Hsien Ming Kao

Research output: Contribution to journalArticlepeer-review

80 Scopus citations


LiFePO4 is a potential cathode material for 4 V lithium-ion batteries. Carbon-coated lithium iron phosphates were prepared using a high surface area carbon to react precursors through a solid-state process, during which LiFePO4 particles were embedded in amorphous carbon. The carbonaceous materials were synthesized by the pyrolysis of peanut shells under argon, where they were carbonized in a two-step process that occurred between 573 and 873 K. The shells were also treated with a proprietary porogenic agent with the goal of altering the pore structure and surface area of the pyrolysis products. The electrochemical properties of the as-prepared LiFePO4/C composite cathode materials were systematically characterized by X-ray diffraction, scanning electron microscope, element mapping, energy dispersive spectroscopy, Raman spectroscopy, and total organic carbon (TOC) analysis. In LiFePO4/C composites, the carbon not only increases rate capability, but also stabilizes capacity. In fact, the capacity of the composites increased with the specific surface area of carbon. The best result was observed with a composite made of 8.0 wt.% with a specific surface area of 2099 m2 g-1. When high surface area carbon was used as a carbon source to produce LiFePO4, overall conductivity increased from 10-8 to 10-4 S cm-1, because the inhibition of particle growth during the final sintering process led to greater specific capacity, improved cycling properties and better rate capability compared to a pure olivine LiFePO4 material.

Original languageEnglish
Pages (from-to)155-162
Number of pages8
JournalJournal of Power Sources
Issue number1
StatePublished - 1 Apr 2009


  • High surface area carbon
  • LiFePO
  • Lithium-ion batteries


Dive into the research topics of 'Study of LiFePO4 cathode materials coated with high surface area carbon'. Together they form a unique fingerprint.

Cite this