Effect of natural aging on the stress corrosion cracking behavior of A201-T7 aluminum alloy

Keyphrases

• Aluminum Alloy 100%
• Cracking Behavior 100%
• Stress Corrosion Cracking 100%
• Natural Aging 100%
• Scanning Electron Microscopy 40%
• Precipitate Free Zone 20%
• Transmission Electron Microscopy 20%
• Enthalpy Change 20%
• Differential Scanning Calorimetry 20%
• Loss Rate 20%
• Slow Strain Rate Test 20%
• As-quenched 20%
• Ductility Loss 20%
• Solute Atoms 20%
• Resistance to Stress 20%
• Polarization Test 20%
• Conductivity Test 20%

Engineering

• Stress Corrosion Cracking 100%
• Cracking Behavior 100%
• Transmissions 25%
• Strain Rate 25%
• Rate Loss 25%
• Solute Atom 25%
• Quenched Alloy 25%
• Enthalpy Change 25%

Material Science

• Aluminum Alloys 100%
• Stress Corrosion Cracking 100%
• Differential Scanning Calorimetry 25%
• Scanning Electron Microscopy 25%
• Transmission Electron Microscopy 25%
• Slow Strain Rate Testing 25%